Electronic Ceramics
-
Pusher Plates
-
Shelf Plates
-
Setters
-
Saggars and Frames
Pusher Plates
We offer a variety of pusher plates to meet diverse customer requirements. They are manufactured through high-pressure molding and high-temperature firing. Therefore, they are stable under thermal, mechanical, and chemical stress at high temperature, and excellent in spalling resistance and creep resistance.
［Pusher plate］
| Brand | Main raw materials | Chemical composition／％ | Bulk density | Apparent porosity % |
Modulus of rupture／MPa | Refractoriness SK |
Linear thermal expansion 1000℃／％ |
||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| Al₂O₃ | SiO₂ | Fe₂O₃ | Na₂O | r.t. | 1400℃ | ||||||
| BP-189A | Alumina | 89.1 | 10.4 | 0.08 | 0.12 | 3.08 | 13.0 | 12.9 | 15.8 | ||
| TDC-987A | Alumina | 86.8 | 12.7 | 0.09 | 0.13 | 3.02 | 12.5 | 14.8 | 16.5 | ||
| MRS-S | Alumina, Mullite | 68 | 29 | 1 | 2.55 | 19.0 | 10.0 | 9.0 | 0.50 | ||
| MAR-S | Alumina, Mullite | 71 | 27 | 0.7 | 2.60 | 17.0 | 12.0 | 10.0 | 38 | 0.49 | |
These data are typical properties subject to reasonable variation and should not be treated as specifications.
Shelf Plates
We offer a variety of shelf plates to meet diverse customer requirements. They are manufactured using high-purity fused alumina and fused mullite as main raw materials, which ensures their stability under high temperatures. Therefore, they are excellent in spalling resistance and bending resistance.
［Shelf plate］
| Brand | Main raw materials | Chemical composition／％ | Bulk density | Apparent porosity % |
Modulus of rupture／MPa | ||||
|---|---|---|---|---|---|---|---|---|---|
| Al₂O₃ | SiO₂ | Fe₂O₃ | Na₂O | r.t. | 1400℃ | ||||
| TDC-SB389A | Alumina | 89.8 | 9.8 | 0.1 | 0.15 | 3.01 | 15.0 | 12.0 | 14.0 |
| TS-387A | Alumina | 87.5 | 12 | 0.09 | 0.13 | 2.96 | 15.0 | 11.5 | 13.5 |
| BD-280A | Alumina | 80.1 | 19.5 | 0.08 | 0.16 | 2.71 | 16.0 | 16.5 | 18.7 |
These data are typical properties subject to reasonable variation and should not be treated as specifications.
Setters
We offer a variety of setters to meet diverse customer requirements. They are manufactured using high-purity alumina, mullite, and cordierite as main raw materials, which ensures their stability under high temperatures. Therefore, they are excellent in spalling resistance and bending resistance.
［Setter］
| Brand | Main raw materials | Chemical composition／％ | Bulk density | Apparent porosity % |
Cold crushing strength MPa |
Modulus of rupture／MPa | Linear thermal expansion 1000℃／％ |
||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Al₂O₃ | SiO₂ | Fe₂O₃ | ZrO₂ | CaO | MgO | Na₂O | SiC | r.t. | 1400℃ | ||||||
| TDC-SB889D | Alumina | 89.4 | 10.2 | 0.1 | 0.12 | 2.89 | 17.8 | 19.2 | 23.4 | ||||||
| TS-290C | Alumina | 90.3 | 9.2 | 0.07 | 0.11 | 2.98 | 17.0 | 15.0 | 19.2 | ||||||
| ZP-595B | Magnesia | 5.3 | 94.1 | 3.10 | 15.5 | 20.0 | (1300℃)11.0 | ||||||||
| HZC-595D | Zirconia | 0.3 | 96 | 3.6 | 4.40 | 23.0 | 10.4 | (1300℃)8.2 | |||||||
| ED-3 | Alumina, Fire clay | 81 | 15 | 0.5 | 2.8 | 2.50 | 25.0 | 25.0 | 13.0 | 6(1300℃) | 0.57 | ||||
| ED-3KF | Alumina, Fire clay | 88 | 9 | 0.5 | 1.4 | 2.70 | 25.0 | 25.0 | 13.0 | 7(1300℃) | 0.42 | ||||
| SLP-SIA82Surface | Alumina | 82.1 | 17.2 | 0.22 | 2.60 | 18.5 | 18.5 | 14.0 | 13.0 | ||||||
| SLP-SIA82Base | Silicon carbide | 7.5 | 0.3 | 91.8 | 2.60 | 18.5 | 18.5 | 14.0 | 13.0 | ||||||
These data are typical properties subject to reasonable variation and should not be treated as specifications.
［Smooth-surface setters］
| Brand | Main raw materials | Chemical composition／％ | Bulk density | Apparent porosity % |
Cold crushing strength MPa |
Modulus of rupture／MPa | Linear thermal expansion 1000℃／％ |
||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Al₂O₃ | SiO₂ | Fe₂O₃ | ZrO₂ | CaO | MgO | Na₂O | SiC | r.t. | 1400℃ | ||||||
| SS-189D | Alumina | 89.3 | 10.2 | 0.1 | 0.14 | 2.80 | 22.3 | 19.0 | 21.0 | ||||||
These data are typical properties subject to reasonable variation and should not be treated as specifications.
Saggars and Frames
We offer a variety of saggars and frames to meet diverse customer requirements. They are manufactured using high-purity alumina, mullite, and cordierite as main raw materials, which ensures their stability under high temperatures. Therefore, they are excellent in spalling resistance, bending resistance, and alkali attack resistance.
［Saggars］
| Brand | Main raw materials | Chemical composition／％ | Bulk density | Apparent porosity % |
Modulus of rupture／MPa | Refractoriness SK |
Linear thermal expansion 1000℃／％ |
Thermal conductivity 1000℃ W/(m·K) |
|||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Al₂O₃ | SiO₂ | Fe₂O₃ | MgO | Na₂O | r.t. | 1400℃ | |||||||
| SB-KP-2 | Alumina | 86.6 | 12.9 | 0.09 | 0.16 | 2.81 | 19.0 | 7.5 | 8.9 | ||||
| TDC-RHKP3 | Alumina | 86.4 | 13.2 | 0.11 | 0.15 | 2.79 | 18.5 | 9.5 | 11.6 | ||||
| ARS-33K-2 | Alumina, Mullite | 84 | 14 | 0.5 | 2.65 | 21.0 | 9.0 | 7(1300℃) | 0.60 | ||||
| CAR | Alumina, Fire clay | 62 | 33 | 1 | 2 | 2.26 | 26.0 | 7.0 | 5(1300℃) | 0.45 | |||
| WM | Alumina, Mullite, Fire clay | 57 | 36 | 0.8 | 2.8 | 2.20 | 25.0 | 8.0 | 5(1300℃) | 0.30 | |||
| WM-60A | Alumina, Mullite, Fire clay | 60 | 36 | 1 | 2.5 | 2.21 | 25.0 | 9.0 | 7(1300℃) | 34 | 0.36 | ||
| B-1 | Alumina, Mullite, Fire clay | 54 | 40 | 0.8 | 4 | 2.10 | 25.0 | 9.0 | 6(1300℃) | 0.40 | 1.7 | ||
These data are typical properties subject to reasonable variation and should not be treated as specifications.
［Frames］
| Brand | Main raw materials | Chemical composition／％ | Bulk density | Apparent porosity % |
Modulus of rupture／MPa | ||||
|---|---|---|---|---|---|---|---|---|---|
| Al₂O₃ | SiO₂ | Fe₂O₃ | Na₂O | r.t. | 1400℃ | ||||
| HW-189B | Alumina | 89.8 | 9.8 | 0.1 | 0.15 | 3.00 | 15.6 | 14.3 | 14.8 |
These data are typical properties subject to reasonable variation and should not be treated as specifications.